| EXXONMOBIL PP 9513 |
 |
| Copolymer |
 |
Random copolymer for non-oriented film.
Contains slip additive and antiblock additive. |
 |
Melt Flow Rate (230'C/2.16 kg): 7.3 g/10 min
Density: 0.9 g/cm 3
Tensile Strength @ Yield (20 in/min, 508 mm/min)
Machine Direction 2.4kpsi 21MPa
Transverse Direction: 2.6kpsi 17MPa
Elongation @ Yield (20 in/min, 508 mm/min) Machine Direction: 5% Transverse Direction: 5%
1% Secant Modulus (0.5 in/min, 12.7 mm/min)
Machine Direction: 78kpsi 531MPa
Transverse Direction: 78kpsi 531MPa
Tensile Strength @ Break (20 in/min, 508 mm/min)
Machine Direction: 8.1kpsi 50MPa
Transverse Direction: 7.5kpsi 46MPa
Elongation @ Break (20 in/min, 508 mm/min) Machine Direction: 690% Transverse Direction: 700%
Haze: 0.6 %
Gloss: 90
Coefficient of Friction: 1 |
|
|
|
|
|