| RED PHOSPHORUS |
 |
| RED PHOSPHORUS |
 |
Molecular formula: P4
Molecular weight: 123.89
Standard executed: GB4947-1990
Capacity: 2000 t/a
Properties:
Auburn amorphorus powder with metallic luster
relative density at 2.34, melting point at 590
soluble in phosphorus tribromide, but insoluble in water or carbon disulphide, liable to burn under chlorine atmosphere, nontoxic, in odorous, without phosphoric light in darkness.
Uses:
Used to make matches, fireworks, chemical agent, phosphoric alloy, and as a raw material for manufacturing organic phosphorus fertilizers, and used in metallurgical industry and organic synthesis as well.
Packing and storage: 50kg iron bucket, 5 ¡Á
10/bag
strike, rolling or throwing strictly forbidden, isolated in storage.
Guaranteed Technical Specifications : No.
Specifications
1st Grade
2nd Grade
1
P4 content% ≥
98.5
97.5
2
Yellow phosphorus% ≤
0.005
0.01
3
Free Acid % ≤
0.5
0.8
4
Moisture%≤
0.25
0.3
5
Fineness (60-mesh) % ≥
70
70
6
Super fineness (100-mesh) %≥
80
7
Super fineness (150-mesh) % ≥80 |
 |
Molecular formula: P4
Molecular weight: 123.89
Standard executed: GB4947-1990
Capacity: 2000 t/a
Properties:
Auburn amorphorus powder with metallic luster
relative density at 2.34, melting point at 590
soluble in phosphorus tribromide, but insoluble in water or carbon disulphide, liable to burn under chlorine atmosphere, nontoxic, in odorous, without phosphoric light in darkness.
Uses:
Used to make matches, fireworks, chemical agent, phosphoric alloy, and as a raw material for manufacturing organic phosphorus fertilizers, and used in metallurgical industry and organic synthesis as well.
Packing and storage: 50kg iron bucket, 5 ¡Á
10/bag
strike, rolling or throwing strictly forbidden, isolated in storage.
Guaranteed Technical Specifications : No.
Specifications
1st Grade
2nd Grade
1
P4 content% ≥
98.5
97.5
2
Yellow phosphorus% ≤
0.005
0.01
3
Free Acid % ≤
0.5
0.8
4
Moisture%≤
0.25
0.3
5
Fineness (60-mesh) % ≥
70
70
6
Super fineness (100-mesh) %≥
80 7
Super fineness (150-mesh) % ≥80 |
|
|
|
|